Hydrothermal process development for the treatment of crocidolite asbestos waste.
The asbestos-containing waste management is a public health topic for countries which have used this mineral. Treatment of chrysotile (white asbestos), a phyllosilicate from serpentine, crocidolite (blue asbestos, first results on this kind of asbestos), one of the five asbestos varieties of amphibole family and asbestos-containing waste conversion process is proposed by using hydrothermal treatment in supercritical water. All samples were treated in an Inconel Batch Reactor. The treatment durations range is from 1 to 6 hours, temperatures range is from 400°C to 750°C, mass concentration range is from 0.02 to 170 mg. mL-1 and pressures are higher than 23 MPa. Ultrapure water is used for sample preparation. This ultrapure water is used to monitor mineral leaching on the aqueous phase and to avoid particle cross-contamination. Transmission electron microscopy analyses were carried out to check the presence or not of asbestos phase. According to these analyses, the best conditions of conversion were 1 hour and 0.02 mg. mL-1 for chrysotile, 3 hours and 0.02 mg. mL-1 for crocidolite and 1 hour and 20 mg. mL-1 for asbestos-containing waste, at T = 750°C. Supercritical water conditions were maintained during the whole treatment. The X-ray diffraction showed that the main phases present after treatments were riebeckite and magnetite (crocidolite), forsterite and enstatite (chrysotile), and calcite, spurrite and gehlenite (asbestos-containing waste). Finally, a scanning electron microscopy analysis was performed to monitor morphological fibre change. The elongated structure, partially fragmented, was found in all samples.
['Nzogo Metoule|C T|CT|', 'Delaby|S|S|', 'Ferrasse|J H|JH|', 'Boutin|O|O|https://orcid.org/0000-0003-1133-122X']
D001194:Asbestos D017638:Asbestos, Crocidolite D017632:Asbestos, Serpentine D008855:Microscopy, Electron, Scanning D014961:X-Ray Diffraction
crocidolite asbestos-containing waste Chrysotile hydrothermal treatment supercritical water