Effect of root canal obturation with calcium silicate materials on pH change in simulated root resorption defects.
This study evaluated the effect of 3 commercially available calcium silicate materials (CSMs) on pH changes in simulated root resorption defects. Simulated root resorption defects were prepared on the facial root surface of 40 mandibular premolars. The depth of each defect was individually calculated to standardize the remaining dentin thickness to 1 mm. Prepared canals were obturated with the 3 CSMs. Ten specimens were kept as controls, filled with unbuffered normal saline. The pH measurements were taken at 1 hour, 6 hours, 1 day, 1 week, 2 weeks, 3 weeks, 1 month, and 2 months. All CSM groups exhibited an initial alkaline pH of 9.0-9.7. The pH decreased to 8.0-8.5 after 2 months of storage. There were no significant differences between pH measurements at other time intervals. The CSM groups exhibited higher pH levels than the control group. The results showed that intracanal placement of the CSMs maintained initial pH levels of 9.0-9.7 inside the simulated resorption defects; these measurements gradually decreased to 8.0-8.5 over the span of 2 months.
['Aggarwal|Vivek|V|', 'Singla|Mamta|M|', 'Miglani|Sanjay|S|', 'Sharma|Ritu|R|']
D017610:Calcium Compounds D003737:Dental Cavity Preparation D006801:Humans D006863:Hydrogen-Ion Concentration D066298:In Vitro Techniques D012389:Root Canal Obturation D012391:Root Resorption D017640:Silicates
root canal obturation calcium silicate pH measurements external root resorption mineral trioxide aggregate