Effects of sodium hypochlorite as dentin deproteinizing agent and aging media on bond strength of two conventional adhesives.
This study evaluated the effect of 10% sodium hypochlorite (NaOCl) as deproteinizing agent and storage media on bond strength (BS) of two etch-and-rinse adhesive systems to dentin. Twenty-eight sound extracted human third molars were divided in four groups (n = 7), according to dentin treatment (conventional etching or etching followed by 10% NaOCl application) and adhesive systems (GB-Gluma 2Bond and OS-One-Step). After dentin treatments and adhesive application, a composite block was built-up on dentin surface and teeth were serially sectioned to obtain bonded sticks specimens. The sticks were submitted to three aging conditions: (24H) 24 hr in water (immediate), (SH) 3 hr of NaOCl accelerated-aging or (1Y) 1 year of water storage. Afterward, submitted to microtensile bond strength test (μTBS), failure modes and adhesive interfaces analyzes. Data were analyzed by two-way analysis of variance (ANOVA) and Tukey's test (α = .05). Dentin deproteinization before bonding significantly reduced μTBS for GB-treated group (p < .05), regardless the aging conditions. Water storage for 1 year (1Y) and NaOCl accelerated-aging (SH) decreased μTBS for both adhesives. Yet, the groups stored in NaOCl (SH) exhibited the lowest BS results (p < .05). Bond strength of deproteinized dentin was dependent on the adhesive system composition and NaOCl accelerated-aging promoted decreased bond strength and further degradation than water storage for 1 year.
['Nima|Gabriel|G|https://orcid.org/0000-0002-0389-4332', 'Cavalli|Vanessa|V|https://orcid.org/0000-0002-9459-1926', 'Bacelar-Sá|Renata|R|https://orcid.org/0000-0002-8803-1316', 'Ambrosano|Gláucia M B|GMB|https://orcid.org/0000-0001-5950-6370', 'Giannini|Marcelo|M|https://orcid.org/0000-0002-7260-5231']
D000269:Adhesives D001840:Dental Bonding D003799:Dental Stress Analysis D003804:Dentin D006801:Humans D008422:Materials Testing D008964:Molar, Third D012973:Sodium Hypochlorite D013718:Tensile Strength D014867:Water
sodium hypochlorite deproteinized dentin bonding systems hybrid layer