Synthesis of Tungsten-Doped Vanadium Dioxide Using a Modified Polyol Method Involving 1-Dodecanol.
The doping of tungsten into VO2 (M) via a polyol process that is based on oligomerization of ammonium metavanadate and ethylene glycol (EG) to synthesize a vanadyl ethylene glycolate (VEG) followed by postcalcination was carried out by simply adding 1-dodecanol and the tungsten source tungstenoxytetrachloride (WOCl4). Tungsten-doped VEGs (W-VEGs) and their calcinated compounds (WxVO2) were prepared with varying mixing ratios of EG to 1-dodecanol and WOCl4 concentrations. Characterizations of W-VEGs by powder X-ray diffraction, differential scanning calorimetry, scanning electron microscopy, and infrared and transmittance spectroscopy showed that tungsten elements were successfully doped into WxVO2, thereby decreasing the metal-insulator transition temperature from 68 down to 51 °C. Our results suggested that WOCl4 variously combined with 1-dodecanol might interrupt the linear growth of W-VEGs, but that such an interruption might be alleviated at the optimal 1:1 mixing ratio of EG to 1-dodecanol, resulting in the successful W doping. The difference in the solar modulations of a W0.0207VO2 dispersion measured at 20 and 70 °C was increased to 21.8% while that of a pure VO2 dispersion was 2.5%. It was suggested that WOCl4 coupled with both EG and 1-dodecanol at an optimal mixing ratio could improve the formation of W-VEG and WxVO2 and that the bulky dodecyl chains might act as defects to decrease crystallinity.
['Lee|Yonghyun|Y|', 'Jung|Sang Won|SW|', 'Park|Sang Hwi|SH|', 'Yoo|Jung Whan|JW|', 'Park|Juhyun|J|0000-0003-1300-5743']
nanoparticles smart windows thermochromic tungsten doping vanadium oxide