In vitro evaluation of osteoblast adhesion, proliferation and differentiation on chitosan-TiO2 nanotubes scaffolds with Ca2+ ions.
Hydrothermally synthesized TiO2 nanotubes (TNTs) were first used as a filler for chitosan scaffold for reinforcement purpose. Chitosan-TNTs (CTNTs) scaffolds prepared via direct blending and freeze drying retained cylindrical structure and showed enhanced compressive modulus and reduced degradation rate compared to chitosan membrane which experienced severe shrinkage after rehydration with ethanol. Macroporous interconnectivity with pore size of 70-230μm and porosity of 88% were found in CTNTs scaffolds. Subsequently, the functionalization of CTNTs scaffolds with CaCl2 solutions (0.5mM-40.5mM) was conducted at physiological pH. The adsorption isotherm of Ca2+ ions onto CTNTs scaffolds fitted well with Freundlich isotherm. CTNTs scaffolds with Ca2+ ions showed high biocompatibility by promoting adhesion, proliferation and early differentiation of MG63 in a non-dose dependent manner. CTNTs scaffolds with Ca2+ ions can be an alternative for bone regeneration.
['Lim|Siew Shee|SS|', 'Chai|Chun Ye|CY|', 'Loh|Hwei-San|HS|']
D002448:Cell Adhesion D002454:Cell Differentiation D049109:Cell Proliferation D048271:Chitosan D007477:Ions D043942:Nanotubes D010006:Osteoblasts D016062:Porosity D054457:Tissue Scaffolds D014025:Titanium
Osteoblast Adsorption Biocompatibility Calcium ions Chitosan-titanium dioxide nanotubes (CTNTs)